AOC, a leading global supplier of high-quality polyester resins, vinyl ester resins, gel coats, and specialty chemicals. Its products are widely used in numerous sectors, including automobiles and trucks, rail transportation, corrosion-resistant pipes and tanks, construction and infrastructure, boats and offshore operations, wind power, chemical processing, and recreational facilities.
AOC China: Jinling AOC Resins Co., Ltd.
Explore the world of AOC Chemicals. We offer a wide range of products, including polyester resins, vinyl ester resins, and gel coats, all manufactured at AOC Resins’ facilities in China. As a leader in innovation within the composites industry, AOC Resins and Gel Coats is committed to meeting every need and delivering exceptional solutions.
AOC Resin Product List
| Product Name | Chemical Structure | Application Characteristics |
|---|---|---|
| Chemical Resistance | ||
| ATLAC 380FP | Modified Flame-Retardant Vinyl Ester | Suitable for a variety of processes; flame-retardant; chemical-resistant; electrostatic wet flue gas scrubbers |
| ATLAC 382H | Propoxy Bisphenol A | Suitable for a wide range of processes; suitable for high-temperature applications; resistant to chemical corrosion |
| ATLAC 430 | Epoxy vinyl ester | Suitable for a wide range of processes; resistant to chemical corrosion (alkali-resistant); Lloyd’s Register certified |
| ATLAC 430YT | Brominated vinyl ester | Suitable for a wide range of processes; flame-retardant; resistant to chemical corrosion; for chimneys and flue ducts in thermal power plants |
| ATLAC 580 | Urethane-modified | Suitable for a wide range of processes; good processing properties; chemical resistance; Lloyd’s Register certified |
| ATLAC 590 | Linear phenolic-modified | High-temperature applications, chemical resistance (solvent and strong acid resistance) |
| ATLAC 590Z | Phenolic-vinyl ester | Excellent resistance to acids, alkalis, salts, and solvents; high-temperature resistance; excellent processing properties |
| ATLAC 590UHT | Phenolic-epoxy-vinyl ester | Extremely high HDT; offers exceptional high-temperature stability and corrosion resistance against organic solvents, strong acids, and oxidizing media such as chlorine gas |
| ATLAC E-NOVA FW2045 | Urethane-modified | Good processing properties, suitable for high-temperature applications, and resistant to chemical corrosion (solvent resistance) |
| ATLAC PREMIUM600 | Epoxy vinyl ester | Styrene-free, storage tank linings, higher resistance to organic chemicals |
| VIPEL F013 | Epoxy vinyl ester | High toughness, excellent crack resistance, suitable for a wide range of processes, and compliant with FDA material requirements |
| VIPEL K022 | Brominated vinyl ester | Meets ASTM E84 Class flame spread rate requirements without synergistic flame retardants |
| Suitable for contact with food and drinking water | ||
| PALATAL A400-976A | M-phenylene | Good water resistance, no plasticizer certification required, suitable for contact with food and drinking water, suitable for soy sauce brewing equipment |
| ATLAC 382H | Propoxybisphenol A | Suitable for a wide range of processes, high-temperature applications, and chemical corrosion resistance; suitable for contact with food and drinking water |
| ATLAC 430 | Epoxy vinyl ester | Suitable for a wide range of processes; resistant to chemical corrosion (alkali-resistant); suitable for contact with food and drinking water |
| SMC/BMC compression molding systems (Items marked with * below were tested using the TM 2261 test method at 130°C) | ||
| PALAPREG H814-902 | Polystyrene | Versatile low-shrinkage additive with good colorability |
| PALAPREG H851-02 | Polymethyl methacrylate | Low-profile additive, high-temperature resistant, suitable for bathroom fixtures and automotive components; effectively resolves fogging issues in automotive headlights |
| PALAPREG H856-902 | Modified polymethyl methacrylate | Enhances the surface gloss of products and resolves the issue of gloss loss in PMMA |
| PALAPREG H870-901 | Polyvinyl acetate | Low-profile additive; high-temperature resistant; enables zero shrinkage in finished products; high gloss |
| PALAPREG H892-02 | Saturated polyester | Low-profile additive for Class A surfaces; negative shrinkage; excellent gloss |
| PALAPREG H852-03 | Saturated polyester | Grade A surface finish, excellent flow properties, for use in low-pressure molding processes |
| PALAPREG H2073-901 | Modified saturated polyester | Can be colored in the vast majority of shades Low-profile additive that enables shrinkage and provides excellent gloss |
| PALAPREG H2681-901 | Specialty saturated polyester | Top-tier Grade A surface, low-profile additive |
| BEYONE 820-H-01 | Modified polystyrene | Zero-shrinkage, colorable |
| BEYONE 875-H-02 | Specialty polyvinyl acetate | Low viscosity, improves toughness, reduces microcracks in products, and features low odor and low volatility |
| PALAPREG P171-903 | Phthalate | Good toughness and water resistance; suitable for low-voltage insulation products and water tank panels |
| PALAPREG P171-903B | Phthalate | Good thickening properties and high mechanical strength; suitable for automotive, electrical, and building materials applications |
| PALAPREG P171-904 | Phthalic | Good heat and water resistance; produces non-porous products; suitable for medium- to high-voltage insulation products |
| PALAPREG P17-902 | Phthalate | Stable thickening, high gloss, passes the GB13115-91 food-grade test, suitable for manufacturing high-performance SMC products |
| PALAPREG P18-03 | Maleic anhydride | High-gloss Grade A surface, thickening stability |
| PALAPREG P0423-902 | Maleic anhydride | For use in combination with Palapreg H2681-901, a low-profile additive with a Grade A surface finish |
| PALAPREG P145-01 | Maleic anhydride | Products exhibit excellent color uniformity. Used in commercial and passenger vehicle components that require high standards for both surface and mechanical properties |
| PALAPREG P6028-901 | Isophthalic/Neopentyl Glycol | Good wetting of glass fibers; resistant to salt, seawater, and high-voltage insulation products; precision injection-molded BMC |
| PALAPREG P6029-901 | Isophthalic/Neopentyl Glycol | Good crack resistance, high heat resistance, excellent water resistance; primarily used in the high-end electronics and electrical markets; superior electrical properties |
| PALAPREG P14-01 | Maleic anhydride | Excellent colorability, high gloss, low shrinkage, and versatile |
| PALAPREG P104-02 | Vinyl ester | Can be thickened with magnesium oxide; excellent corrosion resistance and heat resistance |
| ATLAC XP810-901 | Specialty vinyl ester | Excellent mechanical properties, resistance to thermal degradation, and corrosion resistance |
| Flame-retardant | ||
| SYNOLITE 5001-T-1 | DCPD | Highly filled, highly flame-retardant, low-smoke-density resin with excellent electrical properties; meets the requirements of Cat. 1a (BS 6853), M1 (NFP 92-501), and F0 (NFF 16-101),Class 1/0 (BS 476), and B1 (DIN 4102); suitable for use in the manufacture of various types of vehicles |
| SYNOLITE 5001-W-2 | DCPD | Excellent flame retardancy, very low smoke density, good processability and mechanical properties; meets M1 (NFP92-501), F0 (NFF16-101),HL2 (EN 45545-2R1), and IMO standards; suitable for use in construction, vehicle, and marine vessel manufacturing |
| SYNOLITE 5001-W-903 | Polycyclopentadiene | Excellent flame retardancy, low smoke density; finished products meet EN 45545-2 HL2 (R1) |
| SYNOLITE 8175-W-1 | DCPD | Excellent flame retardancy, low smoke density; products meet the requirements of M2 (NFP92-501), F1 (NFF16-101), and S4/SR2/ST2 (DIN5510) standards; suitable for the manufacture of vehicle structural components |
| SYNOLITE 3175-W-1 | Polycyclic pentadiene | Excellent flame retardancy and low smoke density; products meet the requirements of TB/T3138 and TB/T3237, making them suitable for the manufacture of vehicle structural components |
| SYNOLITE 8175-W-1H | DCPD | Excellent flame retardancy, very low smoke density, good processability and mechanical properties; meets the requirements of the TB/T3237-2010 standard; suitable for the manufacture of building materials, vehicles, and boats |
| SYNOLITE 9001-I-1 | Special Types | Hand lay-up, RTM, and vacuum infusion processes; products meet the S4/SR2/ST2 (DIN 5510) flame retardancy standards; suitable for vehicle manufacturing |
| SYNOLITE 9068-W-1 | DCPD | Excellent flame retardancy, very low smoke density, good processability and mechanical properties; meets Class 1 (BS 476-7) requirements; suitable for construction, vehicle, and boat manufacturing |
| PALATAL HBS-901W | O-phthalic | Highly filled, highly flame-retardant resin with low smoke density |
| PALATAL S320T-954AT | Special-purpose type | Pre-accelerated resin with excellent flame retardancy and low smoke density; products meet the requirements of M2 (NFP92-501), F1 (NFF16-101), and S4/SR2/ST2 (DIN5510) standards; suitable for automotive manufacturing |
| PALATAL S325V-01 | Special Grade | High mechanical properties and low fracture sensitivity; used in fiberglass-reinforced plastic products requiring flame retardancy and low smoke density, such as automotive and train components, construction materials, and electrical accessories |
| Pultrusion | ||
| PALATAL P61-972 | Ortho-phenolic | High strength, high rigidity, and good processability |
| PALATAL P65-972 | O-phthalic | High strength, high rigidity, high reactivity |
| PALATAL A400-901 | Isophthalic | High reactivity, high strength, high heat resistance, good water resistance |
| PALATAL A400-972 | Isophthalic | High heat resistance, high mechanical strength, high elongation at break, good water resistance |
| PALATAL A408-972 | Isophthalic | High reactivity, good crack resistance, wide processing window, enables relatively high pultrusion speeds |
| PALATAL A409-902 | Isophthalic | High reactivity, outstanding heat resistance, good electrical insulation properties |
| PALATAL A409-972 | Metaphthalic | High reactivity, excellent heat resistance, good electrical insulation properties |
| PALATAL A401-902 | Metaphthalic | A resin specifically designed for the pultrusion process that enables faster pultrusion speeds and delivers good mechanical properties. It is suitable for producing pultruded products of various sizes and significantly reduces delamination and bubbling between reinforcing materials during the pultrusion process |
| SYNOLITE 0593-N-972 | Isophthalic | Good water resistance and outstanding wave transmission properties; suitable for antenna radomes |
| SYNOLITE 0175-N-1 | DCPD | Good wetting of fibers and fillers, good mechanical properties |
| ATLAC 430 | Epoxy vinyl ester | Suitable for a variety of processes; resistant to chemical corrosion (alkali-resistant); Lloyd’s Register certified |
| DARON 45 | Epoxy vinyl ester | For high-temperature applications; good wetting properties on carbon fiber |
| PALATAL XF9012 | Specialty Type | High aluminum hydroxide-filled, halogen-free flame retardant, low smoke density, V0 (UL94), Class 1 (BS476-6/7) |
| ATLAC 590UHT | Phenolic-epoxy-vinyl ester | Extremely high HDT; exhibits exceptional high-temperature stability and corrosion resistance against organic solvents, strong acids, and oxidizing agents such as chlorine gas |
| Continuous Board Production | ||
| PALATAL P4L-21 | Ortho-phenolic | UV-resistant, moderate reactivity |
| PALATAL P61L-996 | Phthalate | Excellent wetting properties, light-colored sheets, high rigidity, weather resistance, light stability |
| PALATAL A400L-993 | Isophthalic | High mechanical strength, high heat resistance, good weather resistance, and light stability |
| PALATAL P71V-901 | Ortho/Polycyclic | A general-purpose resin with suitable viscosity and high reactivity; good strength and toughness; suitable for casting and continuous sheet-forming processes; FRP products exhibit low odor and minimal glass fiber grain; cast products show a significant reduction in orange peel |
| SYNOLITET 8388-N-4 | DCPD | Medium reactivity, excellent wetting properties, low shrinkage |
| Marine, hand lay-up, and spray-up | ||
| PALATAL P61TV-956N | Phthalic | Pre-accelerated, thixotropic resin; low viscosity; fast wetting; low exothermic reaction; contains a curing indicator; certified by Lloyd’s Register and the China Classification Society |
| PALATAL P61TV-956L | Ortho-phthalic | Low-styrene-emitting version of the P61TV-956KR series; certified by Lloyd’s Register and the China Classification Society |
| PALATAL P61TV-956KR | Ortho-phthalic | Pre-accelerated, thixotropic resin with low viscosity and high reactivity, excellent wetting properties; certified by Lloyd’s Register and the China Classification Society |
| PALATAL P61TV-956 | Ortho-phthalic | Pre-accelerated, thixotropic resin with high mechanical strength; certified by the China Classification Society |
| PALATAL P61TV-956A | Polycyclopentadiene | Pre-accelerated, pre-thixotropic system; good workability and glass fiber wetting; low shrinkage; minimal glass fiber streaking; low odor; certified by the China Classification Society |
| SYNOLITE 0544-I-2 | Phthalate | Good mechanical properties; certified by Lloyd’s Register and the China Classification Society |
| SYNOLITE 0544-I-2A | O-phthalic | Good mechanical properties; certified by Lloyd’s Register and the China Classification Society |
| SYNOLITE 0544-I-2E | O-phthalic | Good mechanical properties; certified by Lloyd’s Register and the China Classification Society |
| SYNOLITE 0544-I-2EW | Phthalate | Winter version of 0544-I-2E; good mechanical properties; certified by Lloyd’s Register and the China Classification Society |
| SYNOLITE 8388-P-1 | Polycyclopentadiene | Pre-accelerated, pre-thixotropic system; good workability and glass fiber wetting; low shrinkage; minimal glass fiber streaking; low styrene volatilization; DNV certified |
| SYNOLITE 8388-P-1S | Polycyclopentadiene | Pre-accelerated, pre-thixotropic system; good workability and glass fiber wetting; low shrinkage; minimal glass fiber streaking; low styrene volatilization |
| SYNOLITE 8388-P-3 | Polycyclopentadiene | Pre-accelerated, thixotropic system; suitable for hand lay-up and spray-up processes; low shrinkage and low styrene volatilization; low odor, low exothermic reaction; suitable for one-step lay-up molding of thick parts |
| SYNOLITE 8388-P-921 | Phthalic/Polycyclic | Pre-accelerated, thixotropic system; low shrinkage and low styrene content; suitable for multi-pass layup without sanding; good mechanical properties; certified by the China Classification Society |
| ATLAC 430ACT GT60 | Epoxy-vinyl ester modified | Laminates exhibit excellent long-term heat resistance and high dynamic load-bearing capacity; Class 1 resin certification by the China Classification Society |
| ATLAC 430ACT | Epoxy-vinyl ester modified | Laminates offer excellent long-term heat resistance and high dynamic load-bearing capacity |
| PALATAL A400-972 | Isophthalic | High heat resistance, high mechanical strength, high elongation at break, and good water resistance |
| PALATAL A400TV-957 | Isophthalic | High reactivity, high strength, high heat resistance, good water resistance; Class 1 resin certification from the China Classification Society |
| PALATAL A400TV-957S | Isophthalic | Pre-promoted, pre-thixotropic system; good workability and glass fiber wetting; low shrinkage, minimal glass fiber streaking, and low exothermic reaction; suitable for single-shot molding of thick or large parts, or for products requiring high temperature resistance, such as ship hulls, decks, and large flat panels; Class 1 resin certification by the China Classification Society |
| PALATAL P50-952 | Ortho-phenylene | Good wetting properties and water resistance; certified by the China Classification Society |
| PALATAL P6-988KR | Ortho-phthalic | High strength, high toughness, crack resistance, fast curing |
| PALATAL P65TV-958 | O-phthalic/polycyclic | Pre-accelerated, pre-thixotropic system with high reactivity, low shrinkage, low styrene volatilization, and low odor; suitable for products requiring rapid paste formation and rapid demolding |
| PALATAL P65TV-957 | Ortho-phthalic | Pre-accelerated, general-purpose thixotropic resin; features rapid wetting, fast curing, and low styrene volatilization; suitable for products requiring rapid demolding |
| PALATAL P65-901 | O-phthalic | High mechanical strength, high heat resistance, and good water resistance |
| PALATAL 999A | O-phthalic | Good mechanical strength, good wetting properties for glass fiber, low shrinkage; suitable for automotive components |
| SYNOLITE 1777-P-3 | Ortho-phthalic | Contains a low-styrene volatilization inhibitor and a curing indicator; high mechanical strength; low exothermic peak; particularly suitable for thick parts |
| Vacuum Infusion/RTM | ||
| ATLAC 430LV GTXX | Epoxy vinyl ester | Chemical resistance (alkali resistance), good processability, Class 1 resin certification from the China Classification Society |
| PALATAL A400V-998GTXX | Isophthalic | High mechanical strength, good water resistance, and good processability |
| PALATAL P68V-994GTXX | Orthophthalic | High mechanical properties, low heat generation, good processability |
| SYNOLITE 4082-G-33GTXX | Phthalate | High mechanical properties, capable of one-step molding of thicker parts, low heat generation, good product quality, China Classification Society wetting properties, certified |
| SYNOLITE 1967-G-3 | Polycyclopentadiene | Pre-promoted, vacuum-infused resin with no glass fiber streaks or resin bleeds; low viscosity, low shrinkage, high gloss, minimal shrinkage, excellent surface finish on finished products; certified by the Norwegian Ship Classification Society |
| SYNOLITE 8488-G-2 | DCPD | Excellent surface finish for large GRP components; certified by the Norwegian Ship Classification Society |
| SYNOLITE 8488-G-11 | DCPD | Vacuum-infused resin; excellent surface finish for large GRP components; certified by Det Norske Veritas (DNV) |
| Pipes and tanks, filament winding, centrifugal casting, and CIPP (Cured-in-Place Pipe) | ||
| ATLAC 380FP | Modified flame-retardant vinyl ester | Suitable for a variety of processes; flame-retardant; resistant to chemical corrosion and flue gases |
| ATLAC 382H | Propoxy Bisphenol A | Suitable for a wide range of processes; resistant to high-temperature applications and chemical corrosion |
| ATLAC 430 | Epoxy vinyl ester | Suitable for a wide range of processes; resistant to chemical corrosion (alkali-resistant); Lloyd’s Register certified |
| ATLAC 430YT | Brominated vinyl ester | Suitable for a wide range of processes; flame-retardant; resistant to chemical corrosion; for chimneys and flue ducts in thermal power plants |
| ATLAC 590Z | Phenolic vinyl ester | Excellent resistance to acids, alkalis, salts, and solvents; high-temperature resistance; excellent processing properties |
| ATLAC 590UHT | Phenolic-epoxy-vinyl ester | Extremely high HDT; exhibits exceptional high-temperature stability and corrosion resistance against organic solvents, strong acids, and oxidizing media such as chlorine gas |
| ATLAC 490-901 | p-Phenylene | Resistant to high temperatures, acids, salt water, and organic solvents; suitable for underground oil storage tanks |
| VIPELF 774 | p-Xylene | UL-certified to meet the requirements of UL 1316 and UL 1746 Parts II and III |
| PALATAL A410-901 | Metaphthalic acid/neopentyl glycol | High mechanical strength, high-temperature resistance, and resistance to chemical corrosion at high temperatures (e.g., acidic and neutral solutions, strong oxidizing agents, and alcohol-based media); good adhesion to PVC |
| PALATAL A400-972 | Isophthalic | High heat resistance, high mechanical strength, high elongation at break, and good water resistance |
| PALATAL A400-976A | M-phenylene | Good water resistance, certified plasticizer-free, suitable for contact with food and drinking water, suitable for soy sauce brewing equipment |
| PALATAL A400-992 | Isophthalic | High mechanical strength, high-temperature resistance, good water resistance |
| PALATAL P65-901 | Ortho-phthalic | High mechanical strength, high temperature resistance, and good water resistance |
| PALATAL HBS-901 | Phthalate | Good water resistance; HOBAS pipe structural resin |
| PALATAL HLR-901 | Phthalate | Good air-drying properties, high flexibility, HOBAS pipe lining resin, good water resistance, passes the GB13115-91 food-grade test |
| PALATAL A408TV-901 | Specially modified | Suitable for the thermosetting CIPP process used in sewer pipe rehabilitation; good process performance; suitable for large diameters |
| PALATAL Z455TV-901 | Isophthalic | Thermosetting; excellent resistance to water and chemical corrosion; long-term storage stability |
| SYNOLITE 0593-I-3 | Isophthalic | Suitable for the thermosetting CIPP process used in sewer pipe rehabilitation; good processability |
| SYNOLITE 2103-Q-2 | Orthophthalic/neopentyl glycol | UV-curable, complies with DIN 18820/3 and DIN 13121/4, can be thickened with magnesium oxide |
| PALATAL P 92I-908 | Isophthalic/neopentyl glycol | Suitable for light-curing CIPP processes in sewer pipe rehabilitation; good processing properties |
| PALATAL P 92I-909 | Isophthalic acid/neopentyl glycol | Suitable for light-curing CIPP processes in sewer pipe rehabilitation; good process performance |
| ATLAC PREMIUM 600 | Epoxy vinyl ester | Thermosetting, long pot life, styrene-free |
| ATLAC 590T | Phenolic vinyl ester | Excellent resistance to acid, alkali, salt, and solvent corrosion; high-temperature resistance; excellent thermal curing performance for CIPP processes |
| ATLAC E-NOVA RE3475X | Polyurethane-vinyl ester | Excellent resistance to acid, alkali, and salt corrosion at higher temperatures; excellent light-curing CIPP process performance |
| Engineered Stone | ||
| PALATALP4-901 | Phthalate | General-purpose, suitable for various reinforced and non-reinforced applications; particularly suitable for the Breton system |
| PALATALP4-971 | Phthalate | General-purpose, high toughness, high green strength, high filler content, excellent appearance and color |
| PALATAL P5-901 | Phthalate | Resin specifically designed for marble, agate, and SolidSurface |
| PALATAL DL-901 | Isophthalic | High reactivity, high strength, high heat resistance, excellent water resistance, and yellowing resistance |
| PALATAL A400-901 | Isophthalic | High reactivity, high strength, high heat resistance, and good water resistance |
| PALATALA 410-901 | Isophthalic acid/neopentyl glycol | High mechanical strength, high-temperature resistance, and resistance to chemical corrosion at high temperatures (e.g., acidic and neutral solutions, strong oxidizing agents, and alcoholic media); good adhesion to PVC |
| ATLAC 430 | Epoxy vinyl ester | Suitable for a variety of processes, resistant to chemical corrosion (alkali-resistant), Lloyd’s Register certified |
| Chemical anchoring, putty, polyester concrete | ||
| PALATAL K755V-02 | Epoxy vinyl ester | High chemical resistance, amine pre-accelerator |
| PALATAL P64V-957 | Ortho-phthalic | Fast curing, strong adhesion |
| SYNOLITE 2710-U-2 | Tetrahydrophthalic anhydride | Highly filled, fine-grained putty suitable for bonding metal, wood, and natural stone; highly flexible |
| SYNOLITE 6494-U-2 | DCPD | Multi-purpose filler and putty binder; provides appropriate bonding properties and excellent sanding performance |
| SYNOLITE 8388-V-1 | DCPD | Excellent filler wetting properties, high filler loading, thorough curing |
| SYNOLITE 0542-U-2 | Polycyclopentadiene | Semi-rigid resin, excellent air-drying properties and adhesion to substrates, fast and thorough curing, and excellent storage stability |
| SYNOLITE 9262-U-902 | Specially modified | Flexible resin with excellent air-drying sandability and impact resistance; good adhesion and compatibility with water-based paints; specifically designed for high-speed and urban rail systems |
| Mold Resin | ||
| ATLAC430 ACT | Epoxy-vinyl ester modified | Laminates manufactured with Atlac430ACT exhibit excellent long-term heat resistance and high dynamic load-bearing capacity |
| SYNOLITE 1982-W-1 | DCPD | Low exothermic reaction, zero shrinkage, and good processability |
| PALATAL A400TV-957 | Isophthalic | Characterized by high modulus and high elongation at break; exhibits good wetting properties toward glass fibers |
| SYNOLITE 0544--2 | Ortho-phenylene | High mechanical properties; Lloyd’s Register certified |
| Gel coat | ||
| NEOGEL 8373-W-XXXX | Isophthalic/Neopentyl Glycol | Spray gelcoat, excellent water resistance and weather resistance, certified by Lloyd’s Register, Det Norske Veritas, and China Classification Society; used in high-quality products such as boats and sanitary ware |
| NEOGEL 8373-W-XXXX H | Isophthalic/Neopentyl Glycol | Hand-layup gelcoat; excellent water resistance and weather resistance; certified by Lloyd’s Register, Det Norske Veritas, and China Classification Society; used in high-quality products such as boats and sanitary ware |
| NEOGEL 8373-W-XXX AG | Isophthalic/Neopentyl Glycol | Spray gel coat, excellent water resistance, weather resistance, and corrosion resistance, high gloss, used in high-quality products such as bathroom fixtures |
| NEOGEL 8373-W-XXXX UV | Isophthalic/Neopentyl Glycol | Spray gelcoat with excellent water resistance, weather resistance, and corrosion resistance; certified by Lloyd’s Register, Det Norske Veritas, and China Classification Society; used in high-quality products such as boats and sanitary ware |
| NEOGEL 8575-W-XXXX | Isophthalic/neopentyl glycol | Spray gelcoat with excellent overall performance. Outstanding resistance to hot water, weathering, and curing performance in high-humidity environments |
| NEOGEL 8373--0000 | Isophthalic/Neopentyl Glycol | (Spray) Clear gel coat with good overall performance; suitable for sanitary ware, artificial marble, and furniture, among other applications |
| NEOGEL 8373-I-0052B | Isophthalic/neopentyl glycol | (Spray) Non-pre-accelerated clear air-drying gel coat with good overall performance; suitable for sanitary ware, artificial marble, and storage tanks, etc. |
| NEOGEL 8302-W-XXX | Isophthalic | (Spray) gel coat with good overall performance, suitable for automotive and general-purpose FRP applications, etc. |
| NEOGEL 8305-W-XXXX | Isophthalic | (spray) gel coat; excellent water resistance, weather resistance, and overall performance |
| NEOGEL 8305-I-XXXX | Isophthalic/Neopentyl Glycol | (Spray) Clear gel coat, with good overall performance; suitable for sanitary ware, artificial marble, and furniture, etc. |
| NEOGEL 8308-W-XXXX | Isophthalic | (Spray) gel coat with good overall performance, suitable for large-sized products such as engine cowlings and cooling towers |
| NEOGEL XXXX-SR-XXXX | Special Type | Excellent air-drying properties and color consistency; used for large-area repairs |
| NEOGEL XXXX-T-XXXX | Special Type | Excellent air-drying properties and color consistency; for small-area repairs and topcoats |
| NEOGEL 8315-W-XXX | Isophthalic/Neopentyl Glycol | Flame-retardant gel coat with excellent flame retardancy, water resistance, and weather resistance |
| NEOGEL 8315-W-XXXXH | Isophthalic/neopentyl glycol | Flame-retardant gel coat, excellent flame retardancy, water resistance, and weather resistance |
| NEOGEL A400TV-F-XXX | Isophthalic/Neopentyl Glycol | Flame-retardant gel coat, excellent weather resistance and water resistance, good flame retardancy |
| NEOGEL A400TV-F-XXXXH | Isophthalic/Neopentyl Glycol | Flame-retardant gel coat, excellent flame retardancy, water resistance, and weather resistance |
| NEOGEL A400TV-W-XXXX | Isophthalic | Spray gelcoat, good water resistance, weather resistance, and overall performance; approved by the China Classification Society (CCS) for use in boats, sanitary ware, automobiles, etc. |
| NEOGEL A400TL-W-XXXX | Isophthalic | Hand-layup gelcoat; offers good water resistance, weather resistance, and overall performance; certified by the China Classification Society; used in boats, sanitary ware, automobiles, etc. |
| NEOGEL A400TV-S-XXXX | Isophthalic | Spray-applied, sandable gel coat; offers good sandability and overall performance |
| PALATAL A400TL-923 | Isophthalic | Hand-layup transparent non-pre-accelerated gel coat, with good transparency and overall performance |
| PALATAL P6TL-956 | Orthophthalic | Transparent, non-pre-accelerated hand-layup gel coat with good transparency and high heat resistance |
| NEOGEL 8300-W-XXXX | Isophthalic | (Hand-layup) Mold gel coat, high gloss, excellent overall performance |
| NEOGEL 8366-W-XXXX | Epoxy vinyl ester | High-quality mold gel coat with high gloss and high retention rate, long service life, and good corrosion resistance |
| NEOGEL 8393-W-XXXX | Epoxy-vinyl ester | Top-tier, high-quality mold gel coat with high gloss and high retention rate, long service life, and excellent corrosion resistance |