AOC Palatal® P 92I 908 Unsaturated Polyester Resin with Isoprene Neopentyl Glycol for Light-curing Pipe Repair

Home " Product Center " AOC " AOC Palatal® P 92I 908 Unsaturated Polyester Resin with Isoprene Neopentyl Glycol for Light-curing Pipe Repair

Unsaturated polyester resins of m-phenylene neopentyl glycol type for light-curing pipe rehabilitation
P92 I-908 Resin-Based Composites Provide Rapid Rehabilitation of Drainage Lines in No-Excavation Conditions

Characteristic performance

Controlled thickening properties
Controlled process operating time
Quickly impregnates glass fibers
The desired size can be obtained
High long-term service performance retention

typical application

Palatal® P 92 I-908 is particularly suitable for FRP products with outstanding chemical resistance and high mechanical strength in tanks, vessels, hydraulic engineering, piping, shipbuilding, corrosion protection and the electronics industry.
Palatal® P 92 I-908 can be used exclusively for the production of glass fiber reinforced prepregs. This prepreg is ideally suited for the rehabilitation of sewer pipes.

Product Indicators

performances	numerical value	unit (of measure)	Test Methods
exterior condition	open (non-secretive)	–	TM_2265
Solids content, infrared drying	52.0-55.0	%	TM_2033
Viscosity @23℃	650-750	mPa.s	TM_2013
Gel time (25°C to 35°C)	7-11	min	TM_2500
peak exothermic temperature (physics)	180-210	℃	TM_2500

Notes:
Viscosity test: S 2/100 s-1/23°C
Reactivity determined by UV test lamp (300w, Osram)

Typical Properties of Liquid Resins

performances	numerical value	unit (of measure)	Test Methods
Refractive index, 23°C	1.5390	-	2150
flash point	33	°C	TM 2800
Storage period, protected from light, 25 °C	6	moon	–
volumetric shrinkage	8.0	%	Pref-VS

Typical Properties of Pure Resin Casting Body

performances	numerical value	unit (of measure)	Test Methods
tensile strength	85	MPa	ISO 527-2
tensile modulus	3.6	GPa	ISO 527-2
Tensile elongation at break	5.6	%	ISO 527-2
bending strength	150	MPa	ISO 178
bending modulus	4	GPa	ISO 178
Heat Distortion Temperature HDT	107	°C	ISO 75-2
Glass transition temperature Tg	130	°C	ISO 6721-2
Unnotched impact strength	20	kJ/m2	ISO 179

Curing conditions

100g of resin with 1.0 ml CHP-NA (Peroxid-Chemie GmbH) and 0.1 ml cobalt isooctanoate solution (1% diluted into styrene). Post-curing: 100°C for 24 hours

Process Operation Guide

Appropriate additives (e.g., paraffin solutions) must be added in order for products made with Palatal® P 92 I-908 resin to be non-tacky after curing on the natural molding surface in contact with air.
Palatal® P 92 I-908 can be cured with conventional curing agents and low energy UV light (wavelength 365-420nm). If the resin is not exposed to direct sunlight, the operating time duration can be extended to several hours. Curing where direct sunlight or UV exposure is not required can be achieved by adding 0.5 ml of tert-butyl peroxy-2-ethylhexanoate (e.g., Arkema's Luperox 26 or AkzoNobel's Trigonox 21) to 100 g of resin. The addition of small amounts of peroxide is recommended for all applications where low styrene residues are required. If a small amount of peroxide is added to the resin, it can be post cured at 80ºC for a few hours for better performance.

AOC Neogel® 8575-W-XXXX m-phenylene neopentyl glycol gelcoat

Neogel® 8575-W-XXXX is a m-phenylene neopentyl glycol gelcoat that has been used in a wide range of applications such as sanitaryware, swimming pools, marine, water rides, etc., where higher water and weather resistance is required. Characteristic Properties Neogel® 8575-W-XXXX is a m-phenylene neopentyl glycol gelcoat with excellent all-round properties. It is easy to use and has excellent defoaming and mechanical properties. Its long-term hot water resistance (high resistance to foaming), weatherability (resistance to yellowing) and curing in high humidity environments are particularly outstanding. Usage characteristics Neogel® 8575-W-XXXX is a pre-promoted, thixotropic gelcoat. For the following process types, Ne

AOC Palatal® P 92I-909 Unsaturated Polyester Resin with Isoprene Neopentyl Glycol for Light Curing Pipe Repair

Unsaturated polyester resin P92 I-909 of the m-phenylene neopentyl glycol type for light-curing pipe repair offers a solution for the rapid repair of drainage pipes without excavation Characteristics Typical applications Palatal® P 92 I-909 is particularly suitable for applications in tanks, containers, hydraulic engineering, pipelines, shipbuilding, corrosion protection and the electronics industry, which require outstanding chemical resistance and a high degree of mechanical strength. Palatal® P 92 I-909 is specially designed for the production of glass fiber reinforced prepregs. This prepreg is ideally suited for the rehabilitation of sewer pipes. Product Specification Properties Values Units Test Methods

AOC Palatal® P 92I-910 Unsaturated Polyester Resin with Isoprene Neopentyl Glycol for Light Curing Pipe Repair

Unsaturated polyester resin P92 I-910 of the m-phenylene neopentyl glycol type for light-curing pipe repair offers a solution for the rapid repair of drainage pipes without excavation Characteristics Typical applications Palatal® P 92 I-910 is particularly suitable for applications in tanks, containers, hydraulic engineering, pipelines, shipbuilding, corrosion protection and the electronics industry, which require outstanding chemical resistance and high mechanical strength. Palatal® P 92 I-910 is specially designed for the production of glass fiber reinforced prepregs. This prepreg is ideally suited for the rehabilitation of sewer pipes. Product specifications Properties Values Units Test method

Be ready Worked with us?

We are committed to provide customers with customizable products and solutions to win the market through professional technology, fast process, efficient implementation, and become the best service provider in the new material industry.